Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.28 g/cm³ |
| melt mass-flow rate | | ISO1133 | 13 g/10min |
| Melt volume flow rate | | ISO1133 | 11.5 cm3/10min |
| Shrinkage rate | | ISO294-4 | 1.6 % |
| Shrinkage rate | | ISO294-4 | 1.6 % |
| Water absorption rate | | ISO62 | 0.30 % |
| Water absorption rate | | ISO62 | 0.60 % |
| Water absorption rate | | ISO62 | 0.20 % |
| MediumDensity | | | 1.13 g/cm³ |
| SpecificHeatCapacity of Melt | | | 2150 J/kg/°C |
| ThermalConductivityofMelt | | | 0.15 W/m/K |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 76 |
| | ISO868 | 70 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| Limiting Oxygen Index | | ISO4589-2 | 22 % |
| FMVSS flammability | | FMVSS302 | SE |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emissions of Organic Compounds | | VDA277 | 550 µgC/g |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 5.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 5.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 15 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 5.5 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 11 kJ/m² |
| Tensile impact strength | | ISO8256/1 | 57.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 1200 Mpa |
| Tensile stress | | ISO527-2 | 38.0 Mpa |
| Tensile stress | | ISO527-2 | 46.0 Mpa |
| Tensile stress | | ISO527-2 | 34.0 Mpa |
| Tensile stress | | ISO527-2 | 28.0 Mpa |
| Tensile stress | | ISO527-2 | 26.0 Mpa |
| Tensile strain | | ISO527-2 | 19 % |
| Tensile strain | | ISO527-2 | >300 % |
| Nominal tensile fracture strain | | ISO527-2 | 340 % |
| Flexural modulus | | ISO178 | 1150 Mpa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ISO34-1 | 210 kN/m |
| tear strength | | ISO34-1 | 230 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 21 KV/mm |
| | IEC60250 | 4.00 |
| | IEC60250 | 3.70 |
| Dissipation Factor | | IEC60250 | 0.010 |
| Dissipation Factor | | IEC60250 | 0.018 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 105 °C |
| | ISO75-2/A | 45.0 °C |
| brittle temperature | | ISO974 | -84.0 °C |
| Glass transition temperature 2 | | ISO11357-2 | 50.0 °C |
| | ISO11359-2 | 1E-04 cm/cm/°C |
| | ISO11359-2 | 5.44E-08 m²/s |
| vicat | | ISO306/A50 | 213 °C |
| vicat | | ISO306/B50 | 150 °C |
| melting temperature | | ISO11357-3 | 221 °C |
| | ISO11359-2 | 1.5E-04 cm/cm/°C |
| | ISO11359-2 | 9E-05 cm/cm/°C |
| | ISO11359-2 | 1.4E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare