Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 5.0 g/10min |
| Shrinkage rate | | ASTMD955 | 1.5to1.9 % |
| density | | ASTMD792 | 1.11 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTMD2863 | 21 % |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 65.5 MPa |
| elongation | Yield | ASTMD638 | 5.0 % |
| elongation | Break | ASTMD638 | 50 % |
| Flexural modulus | | ASTMD790 | 2210 MPa |
| bending strength | | ASTMD790 | 82.7 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 130 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 190 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+13 ohms·cm |
| dielectric strength | | ASTMD149 | 12 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 60.0 °C |
| melting temperature | | | 216 °C |
| | ASTMD696 | 8.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.