AS 388S
0
CompareTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 7 cm | ||
| Water absorption rate | 0.3 % | ||
| density | 1080 Kg/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 19 Kj/m | ||
| 2.5 Kj/m | |||
| Tensile modulus | 3900 MPa | ||
| tensile strength | 84 MPa | ||
| Tensile fracture elongation | 4 % | ||
| Tensile modulus | 3500 MPa | ||
| 2800 MPa | |||
| Charpy Notched Impact Strength | 21 Kj/m |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | 18 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 3 | ||
| 2.8 | |||
| Dissipation Factor | 50 E-4 | ||
| 80 E-4 | |||
| Volume resistivity | >1E13 Ω.m | ||
| Surface Resistivity | >1E15 Ω | ||
| dielectric strength | 34 KV/mm | ||
| Compared to the Leakage Traceability Index (CTI) | 475 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | 99 ℃ | ||
| 103 ℃ | |||
| vicat | 107 ℃ | ||
| Linear coefficient of thermal expansion | 0.7 E-4/℃ | ||
| combustibility | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.