Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:100.按容量计算的混合比:100 |
| Thermosetting components | | | 按重量计算的混合比:20.按容量计算的混合比:20 |
| Thermosetting mixed viscosity | | ASTM D4878 | 4000 cP |
| stripping time | | 内部方法 | 960to1400 min |
| GelTime | | ASTM D2971 | 23.0 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D4669 | 1.04 g/cm³ |
| Shrinkage rate | | ASTM D2566 | 0.10to0.30 % |
| Weight Percubicinch | | | 17 g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 65 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 5.52 MPa |
| elongation | Break | ASTM D638 | 950 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 无断裂 |
| Suspended wall beam without notch impact strength | | ASTM D256 | 无断裂 |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 29.8 kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.