Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.010 % |
| density | | 内部方法 | 1.68 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.25 % |
| Shrinkage rate | | 内部方法 | 0.55 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ISO 11443 | 260 Pa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | 内部方法 | 150 MPa |
| elongation | Break | 内部方法 | 1.2 % |
| Flexural modulus | | 内部方法 | 11000 MPa |
| bending strength | | 内部方法 | 230 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 4.20 |
| Dissipation Factor | | IEC 60250 | 1E-03 |
| Dissipation Factor | | IEC 60250 | 2E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
| Surface Resistivity | | IEC 60093 | 3E+17 ohms |
| Volume resistivity | | IEC 60093 | 4E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 16 kV/mm |
| dielectric constant | | IEC 60250 | 4.20 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | 内部方法 | 270 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.