PPS A673MX05B TORAY JAPAN

Form：Granules | Grade：Injection grade

Properties:

Chemical resistanceHigh flame retardantHigh temperature resistanHigh mechanical strengthGood thermal stabilityFiller: Glass fiber reinf30% filler by weight

Typical Applications:

Electronic fieldAutomotive sectorMechanical EngineeringChemical field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic field \| Automotive sector \| Mechanical Engineering \| Chemical field
Properties:	Chemical resistance \| High flame retardant \| High temperature resistan \| High mechanical strength \| Good thermal stability \| Filler: Glass fiber reinf \| 30% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	225	Mpa
shear strength	23°C	JISK7214	68.0	Mpa
Friction coefficient			0.25
Taber abraser	1000Cycles	ISO 9352	50.0	mg
tensile strength	Yield,23°C	ISO 527-2	150	Mpa
Tensile strain	Break,23°C	ISO 527-2	2.5	%
Bending modulus	23°C	ISO 178	10000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	255	°C
Melting temperature		ISO 11357-3	278	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	3.3E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD:3.00mm2	Internal Method	0.85	%
Shrinkage rate	Shrinkage rate	MD:3.00mm4	Internal Method	0.20	%
Water absorption rate	23°C,24hr	ISO 62	0.020	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+16	ohms·cm
Dielectric strength		IEC 60243-1	26	KV/mm
Dielectric constant	23°C,1MHz	IEC 60250	3.80
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	114
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
BarFlowLength	320°C,1.00mm	Internal Method	150	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.