ABS TAIRILAC® AG1000 FCFC TAIWAN
636
- Properties:High impact resistanceCharacteristics: Ultra hi
- Usages:safety helmetHelmetFootwearABS pipePipe fittingsheel
- Certificates:ULFDAMSDSTDSProcessingMSDSULRoHSSVHCEnvironmental
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.40to0.70 | % |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 0.90 | g/10min |
| 220°C/10.0kg | ASTMD1238 | 10 | g/10min | |
| 200°C/5.0kg | ISO1133 | 0.90 | g/10min | |
| 220°C/10.0kg | ISO1133 | 10 | g/10min | |
| density | ASTMD792 | 1.03 | g/cm³ | |
| 23°C | ISO1183 | 1.03 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ISO180 | 380 | J/m |
| 23°C,6.35mm | ASTMD256 | 380 | J/m | |
| tensile strength | 23°C | ASTMD638 | 38.2 | Mpa |
| 屈服,23°C | ISO527-2 | 38.0 | Mpa | |
| Bending modulus | 23°C | ASTMD790 | 1910 | Mpa |
| 23°C | ISO178 | 1910 | Mpa | |
| bending strength | 23°C | ASTMD790 | 56.9 | Mpa |
| 23°C | ISO178 | 57.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTMD15253 | 99.0 | °C | |
| ISO306/A | 99.0 | °C | ||
| Hot deformation temperature | 1.8MPa,未退火,12.7mm | ASTMD648 | 84.0 | °C |
| 1.8MPa,Unannealed,12.7mm | ISO75-2/A | 84.0 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 94.0 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 94.0 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.