Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | g/cm³ | 0.13to0.56 |
| Environmental stress cracking resistance | | hr | 0.317to1000 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 49to62 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | | 35to82 |
| transparency | | | 26.9to95.3 |
| Haze ratio | | % | 0.40to21 |
| transmissivity | | % | 68.0to92.3 |
| gloss | | | 30to95 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | % | 14to22 |
| yield | | | 7.45to21.38 Mpa |
| yield | | | 7.66to17.24 Mpa |
| Flexural modulus | | | 260.0to271.03 Mpa |
| fracture | | % | 290to940 |
| yield | | | 175.86to281.38 Mpa |
| fracture | | | 9.45to32.69 Mpa |
| Flexural modulus | | | 0.086to0.52 |
| yield | | % | 2.0to23 |
| fracture | | | 6.97to31.38 Mpa |
| fracture | | % | 47to1000 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Multi axis Instrumented Impact Energy | | J | 8.19to34.30 |
| film | Test Condition | Test Method | Test Result |
|---|
| MD: Fracture | | % | 350to910 |
| fracture | | % | 520to920 |
| film thickness | | mil | 0.94to2.1 |
| TD: Fracture | | % | 660to920 |
| Thin film puncture strength | | n | 1.5506to3.1685 |
| MD | | | 108.28to230.34 Mpa |
| fracture | | | 24.0to50.0 Mpa |
| MD | | g | 0.0to490 |
| TD | | kg·m/cm³ | 1182.64 |
| MD: Surrender | | % | 12to530 |
| MD: Fracture | | | 30.0to57.38 Mpa |
| Thin film puncture strength | | N.m | 347.79 |
| TD | | g | 8.0to810 |
| MD | | | 179.31 Mpa |
| MD: Surrender | | | 8.0to13.24 Mpa |
| MD | | kg·m/cm³ | 1116.45 |
| Initial sealing temperature | | °C | 99to130 |
| TD | | | 200.0 Mpa |
| TD: Yield | | | 8.83to13.31 Mpa |
| TD: Fracture | | | 18.97to45.17 Mpa |
| TD: Yield | | % | 4.0to760 |
| Thin film puncture strength | | kg·m/cm³ | 78.11 |
| TD | | | 115.86to291.03 Mpa |
| yield | | | 5.2to16.97 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | V/mil | 500to760 |
| Volume resistivity | | ohms·cm | 1.0E+5到1.7E+16 |
| dielectric constant | | | 2.10to2.55 |
| Dissipation Factor | | | 1.0E-4到3.0E-3 |
| Test Condition | Test Method | Test Result |
|---|
| tear strength | | n/m | 3938.05to9380.53 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare