ABS 3001MG2A UMG JAPAN

Form：Granules | Grade：Electroplating grade

Properties:

Flame retardantHigh temperature resistan

Typical Applications:

Automotive components

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive components
Properties:	Flame retardant \| High temperature resistan

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			电镀.涂饰
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate			24	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength		ASTM D256/ISO 179	31	kg·cm/cm(J/M)ft·lb/in
Bending modulus		ASTM D790/ISO 178	2.400	kg/cm²(MPa)[Lb/in²]
Bending modulus	Bending modulus			2400	Mpa
Charpy Notched Impact Strength			31	kJ/m²
bending strength	23°C	ISO 178	65.0	Mpa
Bending modulus	23°C	ISO 178	2300	Mpa
tensile strength	23°C	ISO 527-2	41.0	Mpa
Tensile modulus	23°C	ISO 527-2	2200	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	80	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT		80	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.5E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	80.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	24	g/10min
Shrinkage rate	MD：23°C	ISO 294-4	0.40-0.60	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	24.0	cm3/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ISO 2039-2	107

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.