POM LZ750 ASAHIKASEI SUZHOU

Form：Granules | Grade：Injection grade

Properties:

Low friction coefficientHomopolymerwear resistantLubricityLow viscosityHigh mobility

Typical Applications:

Engine partsHousehold goodsEngineering accessoriesShellOutdoor applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Engine parts \| Household goods \| Engineering accessories \| Shell \| Outdoor applications
Properties:	Low friction coefficient \| Homopolymer \| wear resistant \| Lubricity \| Low viscosity \| High mobility

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790	91.0	Mpa
Bending modulus	--	ISO 178	2700	Mpa
Bending modulus	Bending modulus	--	ASTM D790	2800	Mpa
elongation	Break	ISO 527-2	15	%
elongation	elongation	Break	ASTM D638	20	%
tensile strength	--	ASTM D638	60.0	Mpa
tensile strength	tensile strength	Yield	ISO 527-2	62.0	Mpa
Tensile modulus		ISO 527-2	2700	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	100	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	157	°C
Linear coefficient of thermal expansion	MD	ASTMD696	1E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr,50%RH	ASTM D570	0.20	%
Shrinkage rate	MD	Internal Method	1.6-2.0	%
melt mass-flow rate	190°C/2.16kg	ISO 1133	30	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	117
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	86

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.