Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Shrinkage rate | | ISO 294-4 | 0.70 % |
Water absorption rate | | ISO 62 | 0.30 % |
Water absorption rate | | ISO 62 | 0.10 % |
Apparent density | | ISO 60 | 0.65 g/cm³ |
melt mass-flow rate | | ISO 1133 | 6.0 g/10min |
Melt volume flow rate | | ISO 1133 | 5.00 cm³/10min |
Shrinkage rate | | ISO 294-4 | 0.55 % |
flammability | Test Condition | Test Method | Test Result |
---|
Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
Hot filament ignition temperature | | IEC 60695-2-13 | 930 °C |
Hot filament ignition temperature | | IEC 60695-2-13 | 930 °C |
Hot filament ignition temperature | | IEC 60695-2-13 | 930 °C |
Limiting Oxygen Index | | ISO 4589-2 | 36 % |
UL flame retardant rating | | UL 94 | V-0 |
UL flame retardant rating | | UL 94 | V-0 |
Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile strain | | ISO 527-2/5 | 40 % |
Flexural modulus | | ISO 178 | 2900 MPa |
bending strength | | ISO 178 | 100 MPa |
Bending Strain | | ISO 178 | 6.2 % |
Tensile modulus | | ISO 527-2/1 | 3000 MPa |
tensile strength | | ISO 527-2/5 | 64.0 MPa |
tensile strength | | ISO 527-2/5 | 50.0 MPa |
Tensile strain | | ISO 527-2/5 | 5.4 % |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of simply supported beam without notch | | ISO 179/1eU | 150 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179/1eU | 160 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179/1eU | 220 kJ/m² |
Impact strength of cantilever beam gap | | ISO 7391 | 12 kJ/m² |
Multi axis Instrumented Impact Energy | | ISO 6603-2 | 25.0 J |
Multi axis Instrumented Impact Energy | | ISO 6603-2 | 30.0 J |
Multi axis Instrumented Peak Impact Force | | ISO 6603-2 | 4900 N |
Multi axis Instrumented Peak Impact Force | | ISO 6603-2 | 4400 N |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Linear coefficient of thermal expansion | | ISO 11359-2 | 5.5E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 7E-05 cm/cm/°C |
Heat distortion temperature | | ISO 75-2/B | 141 °C |
Heat distortion temperature | | ISO 75-2/A | 132 °C |
vicat | | ISO 306/B50 | 144 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.