NBR NANCAR® 4155 Nantex Industry Co., Ltd.
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 1.00 g/cm³ | ||
| Mooney viscosity | ASTM D1646 | 51 MU | |
| ASTM D1646 | 78 MU | ||
| bound acrylonitrile content | 内部方法 | 40.0 % | |
| stabilizer | Non-staining | ||
| Soluble inMEK | 100 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ASTM D2240 | 76 | |
| ASTM D2240 | 77 | ||
| ASTM D2240 | 78 |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D412 | 10.9 MPa | |
| ASTM D412 | 12.8 MPa | ||
| ASTM D412 | 13.3 MPa | ||
| ASTM D412 | 26.4 MPa | ||
| ASTM D412 | 26.8 MPa | ||
| ASTM D412 | 26.0 MPa | ||
| elongation | ASTM D412 | 590 % | |
| ASTM D412 | 540 % | ||
| ASTM D412 | 520 % | ||
| tear strength | ASTM D624 | 58.0 kN/m | |
| compression set | ASTM D395 | 59 % |
| aging | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Change rate of tensile strength in air | ASTM D573 | -1.0 % | |
| volume change | ASTM D471 | 8.5 % | |
| Change rate of ultimate elongation in air | ASTM D573 | -22 % | |
| Change rate of hardness (Shore) in the air | ASTM D573 | 5.0 | |
| Change rate of tensile strength in air | ASTM D471 | -11 % | |
| ASTM D471 | -26 % | ||
| Change rate of ultimate elongation in air | ASTM D471 | -28 % | |
| ASTM D471 | -28 % | ||
| Change rate of hardness (Shore) in the air | ASTM D471 | 3.0 | |
| ASTM D471 | -5.0 | ||
| volume change | ASTM D471 | -0.20 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat loss | ASTM D5688 | 0.30 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.