ABS

ABS K7050 Shanghai KumhoSunny Plastics Co., Ltd.

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180	无断裂
Impact strength of cantilever beam gap	-30°C	ISO 180	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	15 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB
Atomization	调节后	DIN 75201	<2.0 mg

mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ISO 527-2/50	42.0 MPa
Tensile strain	Break	ISO 527-2/50	20 %
Bending modulus		ISO 178	2200 MPa
bending strength		ISO 178	60.0 MPa
Poisson's ratio		ISO 527	0.39

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	98.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	90.0 °C
Vicat softening temperature		ISO 306/B50	107 °C

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	1.06 g/cm³
melt mass-flow rate	220°C/10.0kg	ISO 1133	8.0 g/10min
Shrinkage rate	23°C	ISO 294-4	0.40to0.70 %
VOCContent-Condition		VDA277	<18.0 µgC/g

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,23°C	ISO 2039-2	108

Supplementary Information	Test Condition	Test Method	Test Result
Ethylbenzene		VDA277	<8.00 µg/g
Odor	Condition:23°C*24h	VDA270	Grade2
	Odor	Condition:40°C*24h	VDA270	Grade3
	Odor	Odor	Condition:80°C*2h	VDA270	Grade3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.