Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.42 g/cm³ |
| melt mass-flow rate | | ISO1133 | 15 g/10min |
| Shrinkage rate | | ISO294-4 | 1.8 % |
| Shrinkage rate | | ISO294-4 | 2.0 % |
| Water absorption rate | | ISO62 | 1.3 % |
| Water absorption rate | | ISO62 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning rate 3 | | ISO3795 | 24 mm/min |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| FMVSS flammability | | FMVSS302 | B |
| atomization | | ISO6452 | 90 % |
| atomization | | ISO6452 | 3.5E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emission | | VDA275 | <8.00 mg/kg |
| Emissions of Organic Compounds | | VDA277 | 3.10 µgC/g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 3000 Mpa |
| Poisson's ratio | | ISO527 | 0.35 |
| Tensile modulus | | ISO527-2 | 3100 Mpa |
| Tensile stress | | ISO527-2 | 71.0 Mpa |
| Tensile strain | | ISO527-2 | 14 % |
| Nominal tensile fracture strain | | ISO527-2 | 25 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 160 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 180 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 8.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO11357-3 | 178 °C |
| | ISO11359-2 | 1E-04 cm/cm/°C |
| | ISO11359-2 | 9E-05 cm/cm/°C |
| | ISO11359-2 | 1E-04 cm/cm/°C |
| | ISO11359-2 | 9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO11359-2 | 160 °C |
| Linear coefficient of thermal expansion | | ISO11359-2 | 30.0 min/mm |
| Heat distortion temperature | | ISO75-2/B | 162 °C |
| Heat distortion temperature | | ISO75-2/A | 96.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.