PP H1030 TASNEE SAUDI

Form：Granules | Grade：Wire drawing grade

Properties:

HomopolymerLow shrinkage

Typical Applications:

ropeSpecial materials for geotextileCarpet backing

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	rope \| Special materials for geotextile \| Carpet backing
Properties:	Homopolymer \| Low shrinkage

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
purpose			地毯.水泥袋.编织袋.土工布.绳索
characteristic			均聚物.低收缩.良好机械性能
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23℃	ISO 180	32	J/m
Bending modulus	1% Secant	ISO 178	1450	Mpa
Rockwell hardness		ISO 2039-2	100	R
elongation		ISO 527-2	10	%
tensile strength		ISO 527-2	33	Mpa
Bending modulus		ASTM D790/ISO 178	1450(MPa)	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	100
tensile strength		ASTM D638/ISO 527	33(MPa)	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	10	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 3146	163	°C
Vicat softening temperature		ISO 306/A50	152	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	102	°C
Vicat softening temperature		ASTM D1525/ISO R306	152	℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	102	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230℃,2.16kg	ISO 1133	3.0	g/10min
density		ASTM D792/ISO 1183	0.9

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.