PC SLX2271T NA9E166T SABIC INNOVATIVE SINGAPHORE

Form：Granules | Grade：High liquidity level

Properties:

Aging resistanceUV resistanceAntistatic

Typical Applications:

Electronic and Electrical ApplicationsLighting applicationsPlastic bagOutdoor applicationsLawn garden equipment

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic and Electrical Applications \| Lighting applications \| Plastic bag \| Outdoor applications \| Lawn garden equipment
Properties:	Aging resistance \| UV resistance \| Antistatic

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ISO 489	1.590
transmissivity	2540μm	ASTM D1003	89.0	%
turbidity	2540μm	ASTM D1003	0.60	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	80.0	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	65	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	65	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.0mm	UL 94	V-2
Burning wire flammability index	1.6mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	825	°C
	Hot filament ignition temperature	2.0mm	IEC 60695-2-13	825	°C
		Hot filament ignition temperature	2.5mm	IEC 60695-2-13	825	°C
		Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	825	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	2300	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2400	Mpa
Bending modulus		ISO 178	2450	Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	2450	Mpa
Tensile strain	Break	ISO 527-2/50	>100	%
elongation	Break	ASTM D638	>100	%
Tensile strain	Yield	ISO 527-2/50	6.0	%
elongation	Yield	ASTM D638	6.0	%
tensile strength	Break	ISO 527-2/50	70.0	Mpa
	tensile strength	Break	ASTM D638	67.0	Mpa
		tensile strength	Yield	ISO 527-2/50	67.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	65.0	Mpa
bending strength		ISO 178	96.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	96.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	140	°C
	Vicat softening temperature	--	ISO 306/B50	139	°C
	Vicat softening temperature	Vicat softening temperature		ASTM D152510	139	°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	124	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124	°C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Outdoor applicability		UL 746C	f2
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.35	%
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	16.0	cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	18	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.