PA6 S RV300 RADIC ITALY

Form：Granules | Grade：Enhanced level

Properties:

High rigidityDimensional stabilityGlass fiber reinforcedenhance

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

High rigidity | Dimensional stability | Glass fiber reinforced | enhance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	68	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
flammability	3.00 mm	FMVSS 302	0	mm/min
Burning wire flammability index	2.0 mm	IEC 60695-2-12	700	°C
UL flame retardant rating	0.8 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	245	Mpa
Bending modulus		ISO 178	8550	Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.1	%
tensile strength	Break	ISO 527-2/1A/5	175	Mpa
Tensile modulus		ISO 527-2/1A/1	9600	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Drying temperature - hot air dryer			80	°C
Drying time - hot air dryer			2.0 to 4.0	hr
Dew Point - Hot Air Drying Machine			-20	°C
Suggested maximum moisture content			0.15	%
Processing (melt) temperature			240 to 280	°C
Mold temperature			80 to 90	°C
Injection speed			中等偏快
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	200	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	215	°C
Melting temperature		ISO 11357-3	220	°C
Vicat softening temperature		ISO 306/B50	210	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0	%
Water absorption rate	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	7.5	%
Shrinkage rate	Flow	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.80	%
density		ISO 1183	1.35	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Surface resistivity		IEC 60093	1.0E+12	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.