PBT SO653 NC010 DuPont, European Union

Form：Granules | Grade：Injection grade

Properties:

Low warpageFiller: Glass beads20%Filler by weight

Typical Applications:

Electronic and electrical componentsAutomotive Applications

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electronic and electrical components \| Automotive Applications
Properties:	Low warpage \| Filler: Glass beads \| 20% \| Filler by weight

Certificates

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-1	22	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.5	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	40	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	4.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	3.5	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	34	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	37	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	24	mm/min
UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	3.0mm	UL 94	HB
		UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	22	%
FMVSS flammability		FMVSS302	SE/B
Fogging-G-value	condensate	ISO 6452	1E-04	g
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23℃, Type 1, Notch A	ISO 180	3.5	KJ/m
Suspended wall beam without notch impact strength	23 ℃, Type 1	ISO 180	37	KJ/m
bending strength	23℃	ISO 178	90	MPa
Tensile modulus	23 ℃, 1.0 mm/min	ISO 527-1	3500	MPa
Tensile strain	23℃, 5 mm/min，Break	ISO 527-1	9.7	%
Tensile stress	Break	ISO 527-1	47	MPa
Charpy Notched Impact Strength	23℃, Type 1, Edgewise, Notch A	ISO 179	3.5	KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃, Type 1, Edgewise, Notch A	ISO 179	3.5	KJ/m
Impact strength of simply supported beam without notch	23℃, Type 1, Edgewise	ISO 179	40	KJ/m
Tensile modulus		ISO 527-2	3500	Mpa
Tensile creep modulus	1000h	ISO 899-1	2400	MPa
Tensile creep modulus	Tensile creep modulus	1h	ISO 899-1	3500	MPa
Tensile strain	Break	ISO 527-2	10	%
Tensile creep modulus	1hr	ISO 899-1	3500	Mpa
tensile strength	Break	ISO 527-2	47.0	Mpa
Tensile creep modulus	1000hr	ISO 899-1	2400	Mpa
bending strength		ISO 178	90.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 Mpa，Unannealed	ISO 75B-1	185	℃
Linear coefficient of thermal expansion	垂直Flow，23 to 55℃(73 to 130°F)	ISO 11359-1	0.00011	cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	平行Flow，23 to 55℃(73 to 130°F)	ISO 11359-1	0.00011	cm/cm/℃
Melting temperature		ISO 3146	225	℃
UL flame retardant rating	3.00 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.50 mm	UL 94	HB
Hot deformation temperature	1.80 Mpa，Unannealed	ISO 75A-1	60	℃
Melting temperature		ISO 11357-3	225	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	165	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	65.0	°C
Vicat softening temperature		ISO 306/B50	195	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.45	g/cm³
Shrinkage rate	TD	ISO 294-4	1.6	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.8	%
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.35	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20	%
density		ISO 1183	1.45
Shrinkage rate	Flow	ISO 294-4	1.8	%
Shrinkage rate	Shrinkage rate	Across Flow	ISO 294-4	1.6	%
Water absorption rate	Sat/23C	ISO 62	0.2	%
Water absorption rate	Water absorption rate	23C/59RH	ISO 62	0.35	%
MediumDensity			1.25	g/cm³
Top out temperature			170	°C
SpecificHeatCapacity of Melt			1850	J/kg/°C
ThermalConductivityofMelt			0.25	W/m/K
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		IEC 60243-1	25	KV/mm
Relative permittivity	100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.70
Dissipation factor	100Hz	IEC 60250	9E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.016
Compared to the anti leakage trace index		IEC 60112	PLC 2
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.