PP 7033N EXXONMOBIL SINGAPORE

100

Form：Granules | Grade：Injection grade

Properties:

High rigidityHigh impact resistanceMiddle flowFast forming cycle

Typical Applications:

Electrical appliancesAutomotive sectorRigid packageSeatChild safetyIndustrial applicationsConsumer goods sectorChild safety seatsConsumer product application fieldApplication in the automotive field

Supplier(1)

Product Description

Certificates(3)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Automotive sector \| Rigid package \| Seat \| Child safety \| Industrial applications \| Consumer goods sector \| Child safety seats \| Consumer product application field \| Application in the automotive field
Properties:	High rigidity \| High impact resistance \| Middle flow \| Fast forming cycle

Certificates

TDS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	-29°C,3.18mm	ASTM D5420	22.8	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.7	kJ/m²
	Charpy Notched Impact Strength	-20°C	ISO 179/1eA	5.3	kJ/m²
		Charpy Notched Impact Strength	0°C	ISO 179/1eA	7.3	kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	13	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256A	210	J/m
	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	3.9	kJ/m²
		Impact strength of cantilever beam gap	-18°C	ISO 180/1A	4.9	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	13	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	1%Secant5	ASTM D790B	1540	Mpa
Bending modulus	Bending modulus	--6	ISO 178	1260	Mpa
Tensile modulus		ISO 527-2/1	1330	Mpa
tensile strength	Yield3	ASTM D638	25.9	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	25.8	Mpa
elongation	Yield3	ASTM D638	5.2	%
elongation	elongation	Yield	ISO 527-2/50	4.0	%
Bending modulus	1%Secant4	ASTM D790A	1360	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	100	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	91.5	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	52.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/2.16kg	ASTM D1238	8.0	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.