Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100 |
| Hardener | | 按重量计算的混合比:25 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.60到1.70 g/cm³ |
| | | 3.7到5.3 Pa·s |
| Curing Time | | | 8.0到12 hr |
| STORAGE STABILITY | | | 25到35 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 87到93 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compression stress | | ISO604 | 80.0到90.0 MPa |
| | 内部方法 | 125 mg |
| Flexural modulus | | ISO178 | 6200到7200 MPa |
| Bending stress | | ISO178 | 63.0到73.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 5.0-6.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 77.0到83.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.