PPO GTX986-74709 SABIC INNOVATIVE NETHERLANDS

Form：Granules | Grade：Conductive grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	10.0	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	3250	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	3000	Mpa
tensile strength	Yield3	ASTM D638	55.0	Mpa
	tensile strength	Yield	ISO 527-2/50	62.0	Mpa
		tensile strength	Break3	ASTM D638	55.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	62.0	Mpa
elongation	Yield3	ASTM D638	5.0	%
	elongation	Yield	ISO 527-2/50	5.0	%
		elongation	Break3	ASTM D638	15	%
		elongation	elongation	Break	ISO 527-2/50	20	%
Bending modulus	50.0mmSpan4	ASTM D790	2700	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2800	Mpa
bending strength	--5,6	ISO 178	90.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan4	ASTM D790	95.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	185	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan9	ISO 75-2/Bf	190	°C
Vicat softening temperature	--	ASTM D152510	192	°C
	Vicat softening temperature	--	ISO 306/B50	198	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	200	°C
Linear coefficient of thermal expansion	MD:-40to60°C	ASTME831	5.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	7E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to60°C	ASTME831	6E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	7.5E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.90	%
melt mass-flow rate	280°C/5.0kg	ASTM D1238	8.5	g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	7.50	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	1.0-1.4	%
Water absorption rate	Saturation,23°C	ISO 62	3.0	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.