Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.30 g/cm³ |
| density | | ASTM D792 | 1.30 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 12 |
| Shore hardness | | ASTM D2240 | 74 |
| Rockwell hardness | R-Scale | ASTM D785 | 12 |
| Shore hardness | | ASTM D2240 | 74 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 91.0 % |
| transmissivity | | ASTM D1003 | 91.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ASTM D635 | 4.4 mm/min |
| burning rate | | ASTM D635 | 4.4 mm/min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 43.6 MPa |
| elongation | Break | ASTM D638 | 190 % |
| tensile strength | | ASTM D638 | 43.6 MPa |
| elongation | Break | ASTM D638 | 190 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 88.1 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 88.1 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 51.8 °C |
| vicat | | ASTM D256 | 77.0 °C |
| Heat distortion temperature | | ASTM D648 | 51.8 °C |
| vicat | | ASTM D256 | 77.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.