PEEK KT-850 NT
0
- Properties:Powderedacid resistantfatigue resistantwear-resistanthigh-puritygood chemical resistanceand convenient processing
- Usages:Electronic and electrical componentsindustrial componentsmedical and health equipment components
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.30 g/cm | |
| melt mass-flow rate | ASTM D1238 | 10 g/10 min | |
| Water absorption rate | ASTM D570 | 0.10 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3650 MPa | |
| tensile strength | ASTM D638 | 96.5 MPa | |
| elongation | ASTM D638 | 5.2 % | |
| elongation at break | ASTM D638 | 20-30 % | |
| Flexural modulus | ASTM D790 | 3680 MPa | |
| bending strength | ASTM D790 | 152 MPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 69.4 J/m | |
| Suspended wall beam without notch impact strength | ASTM D256 | 不断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ASTM D648 | 162 ℃ | |
| Glass Transition Temperature | ASTM D3417 | 150 ℃ | |
| melting temperature | ASTM D3417 | 340 ℃ | |
| ASTM E831 | 0.000043 cm/cm/℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.