Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.32 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.60 % |
| Water absorption rate | | ISO62 | 0.90 % |
| Humidity-Pellets | | ISO1110 | 0.20 % |
| Ash Content | | 内部方法 | 25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 81 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO527-2 | 3.0 % |
| Tensile modulus | | ISO527-2 | 8200 MPa |
| Tensile stress | | ISO527-2 | 155 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 55 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| dielectric strength | | IEC60243-1 | 32 kV/mm |
| CTI | | IEC60112 | 450 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.