Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| stripping time | | | 0.38to1400 min |
| Post curing time | | | 3.5to24 hr |
| STORAGE STABILITY | | | 1.5to8.9 min |
| Thermosetting mixed viscosity | | ASTM D2393 | 344to759 cP |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.998to1.08 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.59to1.5 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 39to98 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | ASTM D695 | 0.0269to1.43 MPa |
| tensile strength | | ASTM D638 | 13.0to38.6 MPa |
| elongation | | ASTM D638 | 5.0to150 % |
| Flexural modulus | | ASTM D790 | 20.7to1230 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 260to270 J/m |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 2.35to19.3 MPa |
| tensile strength | | ASTM D412 | 8.43to21.2 MPa |
| tensile strength | | ASTM D412 | 15.0to24.8 MPa |
| tensile strength | | ASTM D412 | 15.9to51.7 MPa |
| elongation | | ASTM D412 | 110to600 % |
| tear strength | | ASTM D624 | 40.7to124 kN/m |
| tear strength | Split | ASTM D470 | 22 kN/m |
| compression set | | ASTM D395 | 4.0to51 % |
| Shore hardness | | ASTM D2632 | 43to65 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 1.1E-4到1.7E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.