ABS/PMMA BF-0670 BK22101 Samsung Cheil South Korea

Form：Granules

Properties:

High temperature resistanAging resistanceHigh impact resistance

Typical Applications:

Automotive componentsCastersElectronic and electrical componentsElectrical appliances

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive components \| Casters \| Electronic and electrical components \| Electrical appliances
Properties:	High temperature resistan \| Aging resistance \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	7.4	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
	UL flame retardant rating	2.0mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2080	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/50	2500	Mpa
tensile strength	Yield	ASTM D638	49.0	Mpa
	tensile strength	Yield	ISO 527-2/50	52.0	Mpa
		tensile strength	Break	ASTM D638	36.3	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	36.0	Mpa
elongation	Break	ASTM D638	18	%
Tensile strain	Break	ISO 527-2/50	22	%
Bending modulus		ASTM D790	2350	Mpa
Bending modulus	Bending modulus		ISO 178	2360	Mpa
bending strength		ASTM D790	66.7	Mpa
bending strength	bending strength		ISO 178	70.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	90.0	°C
	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	83.0	°C
		Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	92.0	°C
			Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	80.0	°C
				Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	72.0	°C
				Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	86.0	°C
Vicat softening temperature	--	ISO 306/B50	92.090.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	92.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0kg	ASTM D1238	25	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	24	g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.30	%
	Shrinkage rate	TD：3.20mm	ASTM D955	0.30	%
		Shrinkage rate	TD:3.20mm	ISO 2577	0.40	%
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.40	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	114
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	115
Pencil hardness	--6	JISK5401	F
Pencil hardness	Pencil hardness	--7	JISK5401	F

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.