Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Density | | ASTM D792 | 1.528 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.07 % |
| Shrinkage rate | | ASTM D955 | 0.3~0.6 % |
| Shrinkage rate | | ASTM D955 | 0.5~0.9 % |
| Melt mass flow rate | | ASTM D1238 | 29.5 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strength | | ASTM D638 | 118 Mpa |
| Tensile strain | | ASTM D638 | 3.8 % |
| Bending modulus | | ASTM D790 | 8078 Mpa |
| Bending strength | | ASTM D790 | 183 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 73.5 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| Flame retardant grade | | UL-94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dielectric strength | | ASTM D149 | 20 KV/mm |
| Volume resistance | | ASTM D257 | 10000000000000000 Ω-cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature | | ASTM D648 | 205 °C |
| Melting point | | DSC | 223 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.