Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1505 | 0.953 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 0.38 g/10min |
| Resistance to environmental stress cracking | | ASTMD1693 | 25.0 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 66 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| BlowMoldingBarrelTemperature | | | 166to182 °C |
| BlowMoldingHeadTemperature | | | 191 °C |
| BlowMoldingMoldTemperature | | | 16 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTMD638 | 26.9 MPa |
| elongation | Break | ASTMD638 | >500 % |
| Flexural modulus | | ASTMD790 | 1240 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| TensileImpact | | ASTMD1822 | 64.1 J/cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTMD1525 | 128 °C |
| Heat distortion temperature | | ASTMD648 | 73.9 °C |
| brittle temperature | | ASTMD746 | <-60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.