| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.10-0.20 % |
| Water absorption rate | | ASTM D570 | 0.12 % |
| Water absorption rate | | ASTM D570 | 0.23 % |
| Specific volume | | ASTM D792 | 0.658 cm³/g |
| melt mass-flow rate | | ASTM D1238 | 13 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 93 |
| Rockwell hardness | | ASTM D785 | 119 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-1 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 125 Mpa |
| elongation | | ASTM D638 | 3.0 % |
| Flexural modulus | | ASTM D790 | 9650 Mpa |
| bending strength | | ASTM D790 | 186 Mpa |
| Taber abraser | | ASTM D1044 | 32.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D3029 | 6.78 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 67.2 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | >1.0E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 18 KV/mm |
| dielectric constant | | ASTM D150 | 3.53 |
| dielectric constant | | ASTM D150 | 3.53 |
| dielectric constant | | ASTM D150 | 3.48 |
| Dissipation Factor | | ASTM D150 | 1.3E-03 |
| Dissipation Factor | | ASTM D150 | 1.3E-03 |
| Dissipation Factor | | ASTM D150 | 6.7E-03 |
| arc resistance | | ASTM D495 | PLC7 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 4 |
| High arc combustion index (HAI) | | UL 746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI Str | | UL 746 | 130 °C |
| Heat distortion temperature | | ASTM D648 | 154 °C |
| Heat distortion temperature | | ASTM D648 | 146 °C |
| vicat | | ASTM D15255 | 166 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.6E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1050 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.22 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.