Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTMD995 | 0.55 % |
| | ASTMD1238 | 53.00 g/10min |
| density | | ASTMD792 | 1.18 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 104 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 42.2 Mpa |
| elongation at break | | ASTMD638 | 20 % |
| Tensile modulus | | ASTMD638 | 2160 Mpa |
| bending strength | | ASTMD790 | 69.6 Mpa |
| Flexural modulus | | ASTMD790 | 2550 Mpa |
| Impact strength of cantilever beam gap | | ASTMD256 | 280 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 78 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| fire rating | | UL-94 | 3.00mm V-0,5VA |
| fire rating | | UL-94 | 2.50mm V-0,5VA |
| fire rating | | UL-94 | 2.10mm V-0,5VB |
| fire rating | | UL-94 | 1.50mm V-1 |
| fire rating | | UL-94 | 1.00mm V-2 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dielectric Strength | | ASTMD149 | 27 KV/mm |
| | ASTMD257 | 1E+15 Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 84 °C |
| vicat | | ASTM1525 | 84 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.