Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 2.02 g/cm³ |
| melt mass-flow rate | | ISO1133 | 15 g/10min |
| Shrinkage rate | | ISO294-4 | 0.60 % |
| Shrinkage rate | | ISO294-4 | 0.60 % |
| Ash Content | | ISO3451 | 70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 70 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 2400 MPa |
| Bending stress | | ISO178 | 19.0 MPa |
| Tensile stress | | ISO527-2/20 | 11.0 MPa |
| Tensile stress | | ISO527-2/20 | 11.0 MPa |
| Tensile strain | | ISO527-2/20 | 2.0 % |
| Tensile strain | | ISO527-2/20 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 80 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 10 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 50.0 °C |
| vicat | | ISO306/B50 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.