PA12 5533 SP 01 ARKEMA FRANCE

Form：Granules | Grade：Flame retardant enhanced grade

Properties:

High temperature resistanLow temperature resistanc

Typical Applications:

Medical Supplies

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Medical Supplies
Properties:	High temperature resistan \| Low temperature resistanc

Certificates

No Data...

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt density			0.830	g/cm³
Thermal conductivity of melt			0.18	W/m/K
Specific Heat Capacity of Melt			2800	J/kg/°C
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	HB
elastomer	Test Condition	Test Method	Test Result	Test Unit
Permanent compression deformation	23°C	ISO 815	43	%
tear strength		ISO 34-1	110	kN/m
squeeze out	Test Condition	Test Method	Test Result	Test Unit
drying temperature			65 to 75	°C
drying time			4.0 to 6.0	hr
Melt Temperature			210 to 230	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear resistance		ISO 4649	47.0	mm³
Nominal tensile fracture strain		ISO 527-2	> 50	%
Tensile strain	Break	ISO 527-2	> 300	%
Tensile strain	Tensile strain	Yield	ISO 527-2	25	%
tensile strength	100% Strain	ISO 527-2	14.0	Mpa
	tensile strength	10% Strain	ISO 527-2	10.0	Mpa
		tensile strength	Break	ISO 527-2	52.0	Mpa
		tensile strength	tensile strength	Yield	ISO 527-2	12.0	Mpa
Tensile modulus		ISO 527-2	170	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			65 to 75	°C
drying time			4.0 to 6.0	hr
Processing (melt) temperature			200 to 270	°C
Mold temperature			25 to 60	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.7E-4	cm/cm/°C
Melting temperature		ISO 11357-3	159	°C
Vicat softening temperature		ISO 306/B50	142	°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	66.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.60	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	1.2	%
Shrinkage rate	Flow	ISO 294-4	1.2	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.4	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		IEC 60243-1	39	KV/mm
Relative permittivity	100 Hz	IEC 60250	9.00
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	5.00
Dissipation factor	100 Hz	IEC 60250	0.11
Dissipation factor	Dissipation factor	1 MHz	IEC 60250	0.10
Volume resistivity		IEC 60093	3.2E+13	ohms·cm
Surface resistivity		IEC 60093	--	ohms
Compared to the anti leakage trace index		IEC 60112		V
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	Shore D, 15 Sec	ISO 7619-1	50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.