Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | | 1.0 % |
| density | | ISO1183 | 1.31 g/cm³ |
| Shrinkage rate | | | 0.40to0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| FlameRating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 9200 MPa |
| Tensile stress | Break | ISO527-2 | 140 MPa |
| Tensile strain | Break | ISO527-2 | 3.0 % |
| Flexural modulus | | ISO178 | 8300 MPa |
| Bending stress | | ISO178 | 198 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 13 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 41 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | DIN53482 | 1E+15 ohms |
| Volume resistivity | | DIN53482 | 1E+15 ohms·cm |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 2.6E-05 cm/cm/°C |
| | ISO75-2/B | 201 °C |
| | ISO75-2/A | 188 °C |
| | ISO3146 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.