Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
melt mass-flow rate | | ASTM D1238 | 7.0 g/10min |
Shrinkage rate | | 内部方法 | 0.87-0.92 % |
Water absorption rate | | ISO 62 | 0.76 % |
hardness | Test Condition | Test Method | Test Result |
---|
Shore hardness | | ASTM D2240 | 80 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
Limiting Oxygen Index | | ASTM D2863 | 48 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ISO 527-2/50 | 59.0 Mpa |
elongation | | ASTM D638 | 5.0 % |
Tensile strain | | ISO 527-2/50 | 5.0 % |
elongation | | ASTM D638 | 20 % |
Tensile strain | | ISO 527-2/50 | 15 % |
Flexural modulus | | ASTM D790 | 2150 Mpa |
Flexural modulus | | ASTM D790 | 2150 Mpa |
Flexural modulus | | ISO 178 | 2000 Mpa |
bending strength | | ASTM D790 | 94.0 Mpa |
bending strength | | ISO 178 | 98.0 Mpa |
bending strength | | ASTM D790 | 94.0 Mpa |
Taber abraser | | ASTM D1044 | 50.0 mg |
Tensile modulus | | ASTM D638 | 2400 Mpa |
Tensile modulus | | ISO 527-2/1 | 2300 Mpa |
tensile strength | | ASTM D638 | 62.0 Mpa |
tensile strength | | ISO 527-2/50 | 68.0 Mpa |
tensile strength | | ASTM D638 | 53.0 Mpa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO 180/1A | 8.0 kJ/m² |
Impact strength of cantilever beam gap | | ISO 180/1A | 16 kJ/m² |
elastomer | Test Condition | Test Method | Test Result |
---|
tear strength | | ISO 34-1 | 37 kN/m |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Dissipation Factor | | ASTM D150 | 5.4E-03 |
Surface Resistivity | | ASTM D257 | >1.0E+15 ohms |
Volume resistivity | | ASTM D257 | >1.0E+16 ohms·cm |
dielectric strength | | ASTM D149 | 17 KV/mm |
dielectric constant | | ASTM D150 | 3.13 |
dielectric constant | | ASTM D150 | 3.07 |
dielectric constant | | ASTM D150 | 3.04 |
Dissipation Factor | | ASTM D150 | 0.011 |
Dissipation Factor | | ASTM D150 | 6.1E-03 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/Bf | 164 °C |
Heat distortion temperature | | ASTM D648 | 145 °C |
Glass Transition Temperature | | DSC | 200 °C |
vicat | | ISO 306/B120 | 180 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.