Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 1.2 |
| Mold shrinkage rate | | ASTM D-955 | 5-7 10 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 0.15 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D-1238 | 10.5 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D-638 | 69 Mpa |
| Flexural modulus | | ASTM D-790 | 2343 Mpa |
| tensile strength | | ASTM D-638 | 62 Mpa |
| Impact Strength | | ASTM D-256 | 800 J/m |
| Stretching rate | | ASTM D-638 | 130 % |
| bending strength | | ASTM D-790 | 96 Mpa |
| Rockwell hardness | | ASTM D-785 | 118 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D-150 | 3.17 |
| Volume resistivity | | ASTM D-257 | 1.0×10 Ω.cm |
| dielectric constant | | ASTM D-150 | 2.96 |
| Loss factor | | ASTM D-150 | 0.0009 |
| Loss factor | | ASTM D-150 | 0.01 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| UL long-term use temperature | | UL 746B | 130 °C |
| Flame retardancy | | UL 94 | HB |
| vicat | | ASTM D-1525 | 154 °C |
| Flame retardancy | | UL 94 | 1.1 mm |
| Hot deformation strength | | ASTM D-648 | 137 °C |
| | ASTM D-648 | 132 °C |
| linear expansion coefficient | | ASTM E-831 | 6.8×10 1/℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.