Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.47 g/cm³ |
| Apparent density | | ISO 60 | 0.80 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 15.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 1.0 % |
| Shrinkage rate | | ISO 294-4 | 0.20 % |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Shrinkage rate | | ISO 294-4 | 0.10 % |
| Water absorption rate | | ISO 62 | 0.40 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO 7792 | PBT+PET.GHMR.09-070.GF20 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | <10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | <10 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 35 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 35 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | <10 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | <10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 35 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 195 MPa |
| bending strength | | | 3.5 % |
| Tensile modulus | | ISO 527-2/1 | 7500 MPa |
| tensile strength | | ISO 527-2/5 | 120 MPa |
| Tensile strain | | ISO 527-2/5 | 3.2 % |
| Flexural modulus | | ISO 178/A | 7500 MPa |
| bending strength | | ISO 178/A | 195 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 11359-2 | 3E-05 cm/cm/°C |
| | ISO 11359-2 | 9E-05 cm/cm/°C |
| Hot deformation temperature (HDT) | | ISO 75-2/B | 220 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 195 °C |
| vicat | | ISO 306/B120 | 210 °C |
| melting temperature | | ISO 11357-3 | 225to250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.