Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 2577 | 0.20-0.40 % |
| Water absorption rate | | ISO 62 | 5.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 8500 Mpa |
| tensile strength | | ISO 527-2/5 | 125 Mpa |
| Tensile strain | | ISO 527-2/5 | 2.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75-2/B | 210 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 190 °C |
| vicat | | ISO 306/B50 | 210 °C |
| melting temperature | | ISO 11357-3 | 218to222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices