AES DIALAC® ESA20-450 UMG JAPAN
390
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD2.0mm | ISO294-4 | 0.65 | % |
| Melt mass flow rate | 220℃/10Kg | ISO1133 | 22.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ISO2039-2 | 110 | R | |
| tensile strength | 23°C | ISO527-2 | 50 | Mpa |
| Tensile modulus | 23°C | ISO527-2 | 2600 | Mpa |
| bending strength | 23°C | ISO178 | 80 | Mpa |
| Bending modulus | 23°C | ISO178 | 2700 | Mpa |
| Impact strength of simply supported beam gap | 23°C | ISO179/1eA | 11 | kJ/m² |
| -30°C | ISO179/1eA | 4.0 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.80MPa退火 | ISO75-2/Af | 83 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | IEC60093 | 1E+15 | Ω.cm | |
| Insulation strength | IEC60243-1 | 32 | KV/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.