Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTMD570 | 1.3 % |
| Water absorption rate | | | 85-90 ℃ |
| density | | ASTMD792 | 1.19 g/cm³ |
| Shrinkage rate | | ASTMD995 | 0.85-1.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 122 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 100 MPa |
| elongation at break | | ASTMD638 | 6 % |
| Tensile modulus | | ASTMD638 | 5000 MPa |
| bending strength | | ASTMD790 | 160 MPa |
| Flexural modulus | | ASTMD790 | 4500 MPa |
| Charpy Notched Impact Strength | | ASTMD256 | 5 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| fire rating | | UL-94 | 1.60mm HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD257 | 1E+15 Ω.cm |
| Dielectric Strength | | ASTMD149 | 21 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 150 °C |
| | ASTMD648 | 190 °C |
| vicat | Melting Temperature | | 214-220 °C |
| | ASTMD696 | 3E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.