ABS 3904 TRINSEO NETHERLANDS

Form：Granules

Properties:

High impact resistanceLow gloss Low glossHigh impact

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

High impact resistance | Low gloss | Low gloss | High impact

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220℃，10KG	ISO 1133	4.7	g/10min
Melt Volume Flow Rate (MVR)	220℃，10KG	ISO 1133	4.7	cc/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23℃	ISO 180/1A	42	KJ/m
bending strength	2mm/min	ISO 178	70	Mpa
tensile strength	Yield,100mm/min	ISO 527	39	Mpa
Tensile modulus	1mm/min	ISO 527	1820	Mpa
tensile strength	Yield,50mm/min	ISO 527	37	Mpa
Impact strength of cantilever beam gap	-30℃	ISO 180/1A	17	KJ/m
Charpy Notched Impact Strength	23℃	ISO 179/1eA	37	kJ/m²
elongation	100mm/min，Yield	ISO 527	2.8	%
Charpy Notched Impact Strength	23℃	ISO 179/2C(1984)	22	KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃	ISO 179/2C(1984)	12	KJ/m
elongation	50mm/min，Yield	ISO 527	2.6	%
Charpy Notched Impact Strength	-30℃	ISO 179/1eA	18	KJ/m
Bending modulus	2mm/min	ISO 178	1900	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	49N/50℃	ISO 306B	97	°C
Horizontal combustion rate		UL 94	HB
Hot deformation temperature	1.82MPa	ISO 75-1	97	°C
Horizontal combustion rate		ISO 3795	40	mm/min
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate			0.4-0.7	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.