Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.08 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 83 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | DIN5036 | 86.0 % |
| refractive index | | ISO489 | 1.5700 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | | >280 °C |
| SheetTemperature-Forming | | | 165到190 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO527-2 | 1.8 % |
| Flexural modulus | | ISO178 | 3750 MPa |
| Bending stress | | ISO178 | 105 MPa |
| Tensile modulus | | ISO527-2 | 3900 MPa |
| Tensile stress | | ISO527-2 | 60.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 13 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180 | 1.3 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | DIN52612 | 0.17 W/m/K |
| maximum service temperature | | | 85.0 |
| | ISO75-2/B | 101 °C |
| | ISO75-2/A | 98.0 °C |
| vicat | | ISO306/B | 106 °C |
| | DIN53752 | 5.0E-5到7.0E-5 cm/cm/°C |
| specific heat | | ASTMD2766 | 1380 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.