PC 303-10 STYRON US

Form：Granules | Grade：Injection grade

Properties:

heat-resistingtransparentHigh impact resistanceMedium viscosity

Typical Applications:

chipBottle capElectrical fieldElectronic fieldOther sheetsfilm

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	chip \| Bottle cap \| Electrical field \| Electronic field \| Other sheets \| film
Properties:	heat-resisting \| transparent \| High impact resistance \| Medium viscosity

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ISO 489	1.586
transmissivity		ASTM D1003	89.0	%
turbidity		ASTM D1003	1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	13	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	35	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/A	90	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Burning wire flammability index	1.0mm	IEC 60695-2-12	900	°C
	Burning wire flammability index	2.0mm	IEC 60695-2-12	875	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	875	°C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	800	°C
	Hot filament ignition temperature	2.0mm	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	775	°C
Extreme Oxygen Index		ISO 4589-2	26	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ISO 178	2400	Mpa
bending strength		ISO 178	97.0	Mpa
Tensile modulus		ISO 527-2/50	2300	Mpa
tensile strength	Yield	ISO 527-2/50	60.0	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	70.0	Mpa
Tensile strain	Yield	ISO 527-2/50	6.0	%
Tensile strain	Tensile strain	Break	ISO 527-2/50	150	%
Taber abraser		ISO 9352	45	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Ball pressure temperature		IEC 60335-1	>125	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	144	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	141	°C
Vicat softening temperature		ISO 306/B50	149	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183/B	1.20	g/cm³
melt mass-flow rate	300°C/1.2kg	ISO 1133	10	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 11332	9.00	cm3/10min
Shrinkage rate	MD	ISO 294-4	0.50-0.70	%
Water absorption rate	23°C,24hr	ISO 62	0.15	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.32	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	17	KV/mm
Dielectric constant	60Hz	IEC 60250	3.00
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3.00
Relative permittivity	100Hz	IEC 60250	3.00
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.00
Dissipation factor	50Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	2E-03
Compared to the anti leakage trace index	2.00mm,SolutionA	IEC 60112	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ISO 2039-2	73
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.