PA66

PA66 EPR32 Pingdingshan Shenma

Properties:
Features shiny high viscosity product
Usages:
Used for injection molding and extrusion as well as for multifilament extrusion for different purposes as a modified base material particularly suitable for flame retardant modification
Compare

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	73.7 MPa
Impact strength of cantilever beam gap		ISO 180	5.4 KJ/m
Charpy Notched Impact Strength		ISO 179	不断 KJ/m
tensile strength		ISO 527	78.2 MPa
Charpy Notched Impact Strength		ISO 179	7.9 KJ/m
Tensile modulus		ISO 527	2.4 GPa
Bending modulus		ISO 178	0.9 GPa
elongation	Break	ISO 527	30.9 %

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 3146	235-258 ℃
Linear coefficient of thermal expansion		ASTM D696	7.5 10
melt mass-flow rate		ISO 1133	3.4 g/10min
Hot deformation temperature	HDT	ISO 75	71.6 ℃

Physical properties	Test Condition	Test Method	Test Result
Impurities and color particles		QB	≤0.017 %
Relative viscosity		QB	3.20±0.01
Water absorption rate	干切片	GB	≤700 ppm
Terminal amino content		QB	36±3 Meq/Kg
Terminal carboxyl content	COOH	QB	56±3 Meq/Kg

Electrical performance	Test Method	Test Result
Volume resistivity	IEC 93	-- Ω.cm
Dielectric strength	IEC 243	-- Kv/mm
UL flame retardant rating	UL 94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.