PA612 Zytel® FE5382 BK276 DUPONT USA
189
- Properties:Thermal stability
- Usages:Electronic fieldElectrical field
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.32 | ||
| Shrinkage rate | ASTM D955 | 0.3(流动，3.2mm) | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fracture stress | ISO 527 | 170 | Mpa | |
| Fracture strain | ISO 527 | 2.5 | % | |
| Tensile modulus | ISO 527 | 9800 | Mpa | |
| Bending modulus | ISO 178 | Mpa | ||
| Gap impact strength | -，-40℃ | ISO 179/1eA | kJ/m² | |
| -，23℃ | ISO 179/1eA | kJ/m² | ||
| elongation at break | ASTM D412/ISO 527 | 2.5 | % | |
| Tensile modulus | ASTM D412/ISO 527 | 9800 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D412/ISO 527 | 170 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 8400 | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 12 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 10(-40℃) | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 200 | ℃（℉） | |
| melting point | 218 | ℃（℉） | ||
| Hot deformation temperature | 1.8Mpa | ISO 75 | ℃ | |
| Melting temperature | 10℃/min | ISO 11357-1,-3 | ℃ | |
| Flame retardant grade | 0.75mm | IEC 60695-11-10 | HB | |
| 0.75mm | UL94 | HB | ||
| Temperature index | RTI, Electrical，0.75mm | ℃ | UL 746B | |
| RTI, Impact，0.75mm | ℃ | UL 746B | ||
| RTI, Strength，0.75mm | ℃ | UL 746B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.