Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| stripping time | | | 300 min |
| stripping time | | | 120 min |
| Thermosetting mixed viscosity | | | 500 cP |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | White |
| MixRatiobyWeight(PBW) | | | 2.0 |
| MixRatiobyWeight(PBW) | | | 1.0 |
| MixRatiobyVolume(PBV) | | | 2.0 |
| MixRatiobyVolume(PBV) | | | 1.0 |
| density | | | 1.10 g/cm³ |
| density | | | 1.10 g/cm³ |
| Viscosity | | | 0.10 Pa·s |
| Viscosity | | | 1.3 Pa·s |
| Curing Time | | | 16 hr |
| Curing Time | | | 1.7E+02 hr |
| Curing Time | | | 10 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | | 49.6 MPa |
| elongation | Break | | 6.0 % |
| Shore hardness | | | 70 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | | 1390 MPa |
| bending strength | | | 57.2 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 84 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | 78.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare