PA6T TKR4355G7 BASF GERMANY

112

Form：Granules | Grade：Injection grade

Properties:

High rigidityThermal stability

Typical Applications:

Automotive ApplicationsEngineering accessories

Supplier(3)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Engineering accessories
Properties:	High rigidity \| Thermal stability

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	HB
Polymer Abbreviation			PA6T/6-GF35
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	12000	Mpa
tensile strength	Break	ISO 527-2	210	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
Tensile creep modulus	1000 hr	ISO 899-1	--	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			110	°C
drying time			8.0	hr
Suggested maximum moisture content			0.15	%
Hopper temperature			80	°C
Temperature at the rear of the barrel			300	°C
Temperature in the middle of the barrel			310	°C
Temperature at the front of the material cylinder			320	°C
Spray nozzle temperature			320	°C
Processing (melt) temperature			310 to 330	°C
Mold temperature			80 to 120	°C
Residence Time			< 5.0	min
Screw speed			< 18	m/min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	245	°C
Melting temperature		ISO 11357-3	295	°C
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	1.5E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ISO 11359-2	5.0E-5 到 6.0E-5	cm/cm/°C
specific heat			1300	J/kg/°C
thermal conductivity		DIN 52612	0.28	W/m/K
Temperature index - at 50% loss of tensile strength	--5	IEC 60216	160	°C
Temperature index - at 50% loss of tensile strength	Temperature index - at 50% loss of tensile strength	--6	IEC 60216	135	°C
Maximum operating temperature	短周期操作		270	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Apparent density			0.70	g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.0	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30	%
Water absorption rate	Saturation, 23°C	ISO 62	4.3 to 5.3	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.80 to 1.2	%
Stickiness	96% H2SO4	ISO 307	130	cm³/g
Mold Shrinkage - Constrained			0.35	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	--	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	33	KV/mm
Relative permittivity	1 MHz	IEC 60250	4.20
Dissipation factor	1 MHz	IEC 60250	0.020

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA6T TKR4355G7 BASF GERMANY

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index