Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 1.0 g/10min |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 滚塑成型 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 61 |
| Haze ratio | | ASTM D1003 | 7.1 % |
| film | Test Condition | Test Method | Test Result |
|---|
| Secant modulus | | ASTM D882 | 205 Mpa |
| Secant modulus | | ASTM D882 | 230 Mpa |
| tensile strength | | ASTM D882 | 9.64 Mpa |
| tensile strength | | ASTM D882 | 10.4 Mpa |
| tensile strength | | ASTM D882 | 57.5 Mpa |
| tensile strength | | ASTM D882 | 53.1 Mpa |
| elongation | | ASTM D882 | 520 % |
| elongation | | ASTM D882 | 730 % |
| Dart impact | | ASTM D1709A | 190 g |
| Elmendorf tear strength | | ASTM D1922 | 120 g |
| Elmendorf tear strength | | ASTM D1922 | 560 g |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.985-1.0 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 130-142 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648/ISO 75 | 85 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.