PEKK OXPEKK® MG200 Oxford Performance Materials, Inc.
0
- Usages:Medical and nursing supplies
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.31 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 100to120 g/10min | |
| Shrinkage rate | ASTM D955 | 1.4 % | |
| Water absorption rate | ASTM D570 | <0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 88 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 138 MPa |
| Break | ASTM D638 | 110 MPa | |
| elongation | Yield | ASTM D638 | 4.0 % |
| Flexural modulus | ASTM D790 | 4550 MPa | |
| bending strength | ASTM D790 | 193 MPa | |
| compressive strength | ASTM D695 | 207 MPa | |
| shear strength | ASTM D732 | 138 MPa | |
| elongation | Break | ASTM D638 | 12 % |
| Tensile modulus | ASTM D638 | 4410 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 53 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 175 °C | |
| Glass Transition Temperature | DSC | 163 °C | |
| melting temperature | DSC | 360 °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 2.1E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.