PBT

PBT LONGLITE® PBT 7030-104X Chang Chun Plastics Co., Ltd. (CCP Group)

Properties:
Filler glass fiber reinforced material 30% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.5 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2	10000 MPa
tensile strength	Break,23°C	ISO 527-2	125 MPa
Tensile strain	Break,23°C	ISO 527-2	2.5 %
Bending modulus	23°C	ISO 178	7500 MPa
bending strength	23°C	ISO 178	190 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	160 °C
Melting temperature		ISO 11357-3	225 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.47 g/cm³
Shrinkage rate	TD	ISO 294-4	0.50to1.1 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.10to0.30 %
Melt viscosity	260°C	ISO 11443	220 Pa·s

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+13 ohms
Volume resistivity		IEC 60093	1E+14 ohms·cm
Dielectric strength	2.00mm	IEC 60243-1	22 kV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.