PPS A3 Dongguan Mingji

Form：Powder | Color：black | Grade：Reinforced and Toughened Grade | Filler：glass fibre 30 %

Properties:

enhanceHigh temperature resistanHigh rigidityFireproof V0Acid and alkali resistantwear resistant

Typical Applications:

Electronic accessoriesEngine partsbearingWear resistant accessorieFaucet componentsEjector

Supplier(0)

Product Description

Certificates(1)

Datasheet

Alternative(1)

Product Description

Typical Applications:	Electronic accessories \| Engine parts \| bearing \| Wear resistant accessorie \| Faucet components \| Ejector
Properties:	enhance \| High temperature resistan \| High rigidity \| Fireproof V0 \| Acid and alkali resistant \| wear resistant
Color:	black
Form:	Pellets
Filler:	glass fibre 30%

Certificates

SGS

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	2.2	%
tensile strength		ASTM D638/ISO 527	155	kg/cm²(MPa)[Lb/in²]；
Bending modulus		ASTM D790/ISO 178	14000	kg/cm²(MPa)[Lb/in²]；
bending strength		ASTM D790/ISO 178	270	kg/cm²(MPa)[Lb/in²]；
Izod Notched Impact Strength		ASTM D256/ISO 179	11	kg·cm/cm(J/M)ft·lb/in
Tensile elongation at break (elongation at break)		ASTM D638/ISO 527	2.3	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL94	V-0
Hot deformation temperature		ASTM D648/ISO 75	260	℃（℉）
melting point			278	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	3	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Molding shrinkage rate		ASTM D955	0.22	%
density		ASTM D792/ISO 1183	1.69
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	0.02	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance		ISO 14782	123

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.